Fireproof Refractory Insulating Fire Brick Fused Silica Bricks High Compressive Strength
-
Parameters
-
Comments
| SiO2 %,≥: | 94.5 | CaO %: | 2.2 |
|---|---|---|---|
| Refractoriness °C: | 1790 | Apparent Porosity %: | 22(24) |
Fireproof Refractory Insulating Fire Brick , Fused Silica Bricks High Compressive Strength
Silica Brick Description
High quality silica brick is made of silicon raw material, the content of SiO2 is above 95%. And the content of Al2O3 is below 1.0%.
Silica Brick Advantage:
1) Silicon oxide is above 95%.
2) Good acid erosion resistance.
3) High softening point with temperature.
4) No shrink in burn repeatedly.
5) Temperature of refractoriness under load is above 1650º C .Stable Capability, High Quality.
Application of silica brick:
They are widely used for hot blast furnace, coke oven, and glass furnace. The products can be made according to customers' requirement.
Silica Bricks specification:
| Item | Coke Oven Silica Brick | Glass Furnace Silica Brick | Hot Blast Stove Silica Brick | |
| JJG-94 | JBG-95 | JBG-96 | JRG-95 | |
| SiO2 % | 94.5 | ≥95 | ≥96 | 95 |
| Fe2O3 % | 1.5 | ≤1.0 | ≤1.0 | 1.3 |
| CaO % | 2.5 | 2.2 | 2.2 | |
| Refractoriness °C | 1790 | 1790 | 1790 | 1790 |
| Refractoriness under load T1,°C | 1650 | 1650 | 1660 | 1650 |
| Apparent porosity % | 22(24) | 22(24) | 22(24) | 22(24) |
| Cold crushing strength Mpa | 40(35) | 35(30) | 35(30) | 35(30) |
| True Density g/cm3 | 2.33 | 2.32 | 2.33 | 2.34 |
| Thermal Expansion % |
1000°C 1.28(1.30) |
1000°C ≤1.25 |
1000°C ≤1.25 |
1000°C 1.26 |
| Residual Quartz % | 1.0 | 1.0 | 1.0 |
1.0 |