AZS 33 Zirconia Corudum Fire Clay Bricks For Glass Furnace High Strength

Rating:
Get Quotation
X

Contact Seller

Al2O3: 40% ZrO2: 34%
SiO2: 14% Na2O: 1.6%
Bulk Density: 3.95g/cm3 Certificate: CE
Origin: China

 

AZS 33 Zirconia Corudum Fire Clay Bricks For Glass Furnace , High Strength

 

Future

 

1 .Casted by melting raw material in the mold, then cooling and solidification.

2. Strong glass corrosion resistance and high thermal shack stability.

3.  Good wear-resistance,dregs-resistance and alkali corrosion resistance.

4. High-purity raw material, barely no pollution.

5. Top quality, long service time.

Specification

Reference Index AZS-33# AZS-36# AZS-41#
Chemical Composition Al2O3
ZrO2 32-34% 35-37% 40-42%
SiO2 ≤16.0% ≤14% ≤13.0%
Na2O ≤1.5% ≤1.6% ≤1.3%
Fe2O3+TiO2+CaO
+Ma2O+K2O+B2O3
≤2.5% ≤2.5% ≤2.5%
Bulk density( Dense part) 3.85g/cm3 3.95g/cm3 4.0g/cm3
Corrosion resistance of glass melt
(common glass,1500℃*36h)
≤1.6mm/24h ≤1.5mm/24h ≤1.3mm/24h
Bubbling separate
(common glass,1300℃*10h)
≤2.0% ≤1.5% ≤1.3%

AZS 33 Zirconia Corudum Fire Clay Bricks For Glass Furnace , High Strength

AZS 33 Zirconia Corudum Fire Clay Bricks For Glass Furnace , High Strength