Fire Resistant Zircon Mullite Brick For Cement Kiln / Hot - Blast Stove

Parameters
Comments (0)

Parameters
Comments

Your Name: Your Comment: Captcha

Fire Resistant Kiln Refractory Zircon Mullite Brick For Cement Kiln And Hot-blast Stove

Quick Detail:

1, High strength
2, Good thermal shock resistance
3, High temperature erosion resistance
4, Good slag resistance

Description:

Zircon mullite brick selected high quality mullite sand and zircon powder as its main raw material. Molded by high pressure and sintered by high temperature , the zircon-mullite brick has such advantages as high bulk density, high strength, good thermal shock resistance, high temperature erosion resistance and good slag resistance. It is mainly used in long-life orifice rings, tank bottom, tank superstructure, perfume-bottle feeder, covers for working tanks and soda lime glass.

Applications:

The zircon mullite brick is mainly used in long-life orifice rings, tank bottom, tank superstructure, isostatically pressed, electrode blocks, perfume-bottle feeder, covers for working tanks and soda lime glass, etc.

Specifications:

Item		ZM-17	ZM-20 (Zirmul)	ZM-25 (Vista)	ZM-30	ZM-11
Chemical composition	Al2O3	≥70	≥59	≥57	≥47	≥72
	ZrO2	≥17	≥19.5	≥25.5	≥30	≥11
	SiO2	≤12	≤20	≤14.5	≤20	≤12
	Fe2O3	≤0.5	≤0.5	≤0.5	≤0.3	≤0.5
Apparent Porosity％		≤17	≤17	≤17	≤18	≤17
Bulk Density g/cm3		≥3.15	≥2.95	≥3.15	≥3.10	≥3.1
Cold Crushing Strength Mpa		≥90	≥100	≥120	≥100	≥90
0.1Mpa Refractoriness Under Load T0.6 ℃		≥1650	≥1650	≥1650	≥1650	≥1630
Permanent Linear Change On Reheating(%)1500℃X2h		±0.3	±0.3	±0.3	±0.3	±0.3
20-1000℃ Thermal Expansion % (x 10-6)		0-0.6	0-0.6	0-0.6	0-0.6	0-0.6
Thermal Conductivity (Average800℃) W / (M.K)		≤ 2.19	≤ 2.19	≤ 2.1	≤ 2.1	≤ 2.19
Pyrometric Cone Equivalent ℃ SK		31	31	31	31	31